Preparation of Si₃N₄-SiC composites by microwave route

Abstract

Si₃N₄-SiC composites have been microwave sintered using β-Si₃N₄ and β -SiC as starting materials. Si₃N₄ rich compositions (95 and 90 vol.% Si₃N₄) have been sintered above 96% of theoretical density without using any sintering additives in 40 min. A monotonic decrease in relative density is observed with increase in SiC proportion in the composite. Decrease in relative density has manifested in the reduction of fracture toughness and microhardness values of the composite with increase in SiC content although the good sintering of matrix Si₃N₄ limits the decrease of fracture toughness. Highest value of fracture toughness of 6×1 MPa m^1/2 is observed in 10 vol.% SiC composite. Crack propagation appears to be transgranular in the Si₃N₄ matrix and the toughening of the composites is through crack deflection around hard SiC particles in addition to its debonding from the matrix.