Bonding interactions and stability assessment of biopolymer material prepared using type III collagen of avian intestine and anionic polysaccharides

Abstract

The present study demonstrate bonding interactions between anionic polysaccharides, alginic acid (AA) and type III collagen extracted from avian intestine used for the preparation of thermally stable and biodegradable biopolymer material. Further the study describes, optimum conditions (pH, temperature and NaCl concentration) required for the formation of fibrils in type III collagen, assessment on degree of cross-linking, nature of bonding patterns, biocompatibility and biodegradability of the cross-linked biomaterial. Results revealed, the resultant biopolymer material exhibit high thermal stability with 5-6 fold increase in tensile strength compared to the plain AA and collagen materials. The degree of cross-linking was calculated as 75%. No cytotoxicity was observed for the cross-linked biopolymer material when tested with skin fibroblast cells and the material was biodegradable when treated with enzyme collagenase. With reference to bonding pattern analysis we found, AA cross-linked with type III collagen via (i) formation of covalent amide linkage between -COOH group of AA and ε-NH₂ group of type-III collagen as well as (ii) intermolecular multiple hydrogen bonding between alginic acid -OH group with various amino acid functional group of type-III collagen. Comparisons were made with other cross-linking agents also. For better understanding of bonding pattern, bioinformatics analysis was carried out and discussed in detail. The results of the study emphasize, AA acts as a suitable natural crosslinker for the preparation of wound dressing biopolymer material using collagen. The tensile strength and the thermal stability further added value to the resultant biopolymer.