Ojha, S. N. ; Anantharaman, T. R. ; Ramachandrarao, P. (1982) Solidification of undercooled cadmium-zinc eutectic melts Journal of Materials Science, 17 (9). pp. 2644-2648. ISSN 0022-2461
Full text not available from this repository.
Official URL: http://www.springerlink.com/content/j41323j28w7571...
Related URL: http://dx.doi.org/10.1007/BF00543899
Abstract
Molten specimens of Cd-Zn eutectic alloy (26.50 at.% Zn) were undercooled by the glass-slag technique using glass-forming ZnCl2 as the slag. The microstructure of the solidified samples, weighing about 20 g each, was found to be a function of the undercooling produced. At lower undercoolings the microstructure consisted of supersaturated primary cadmium dendrites co-existing with the eutectic, while at higher coolings duplex structures were observed. Possible causes for the differences in microstructure are discussed with due importance given to the recorded recalescence effects.
| Item Type: | Article |
|---|---|
| Source: | Copyright of this article belongs to Springer. |
| ID Code: | 57489 |
| Deposited On: | 27 Aug 2011 14:58 |
| Last Modified: | 27 Aug 2011 14:58 |
Repository Staff Only: item control page