The effect of synthesis procedure on the structure and properties of palladium/polycarbonate nanocomposites

Abstract

In this paper, we compare two procedures for the synthesis of palladium (Pd)/polycarbonate (PC) nanocomposites as well as their morphological, optical, thermal and electrical properties. Pd nanoclusters were produced by the reduction of palladium chloride using a variation of Brust's method. Discrete Pd nanoclusters of ^~ 15 nm size were formed in the absence of PC in the reaction mixture (ex situ method) while agglomeration of Pd nanoclusters was noticed in the presence of PC in the reaction mixture (in situ method). Fourier transform infrared spectroscopy (FTIR) suggests nanoparticle-polymer interactions and polymer conformational changes in the in situ nanocomposite films. Even after having the same Pd content, the ex situ nanocomposites films were found to transmit more light than the in situ nanocomposites. The glass transition temperature (T_g), decreased by ~ 16 ° C for both the ex situ and in situ samples. Thermogravimetric analysis (TGA) indicated that the presence of Pd nanoclusters significantly improved the thermal stability of the nanocomposites, as evidenced by the enhanced onset of degradation by ^~ 20 °C and 40 °C for the in situ and ex situ nanocomposites, respectively. The electrical conductivity measurement shows a dramatic difference between these nanocomposites with a significantly higher value for the in situ nanocomposite (resistivity = 2.1 × 10⁵ Ω m) compared to the ex situ nanocomposite (resistivity = 7.2 × 10¹³ Ωm).