Isotope effect and correlation factor for the diffusion of cadmium in silver

Abstract

Isotope effect studies for the diffusion of Cd in silver single crystals are made using the isotope pair Cd^115m and Cd¹⁰⁹ in the temperature region 730 to 906 ° C. The enhancement factor 'b' is measured in dilute Ag-Cd alloy upto ≈ 3 at% cadmium at 860 and 924 ° C. The data from the isotope effect and enhancement factor are combined to calculate the jump frequency ratios, using Howard and Manning's calculations. The correlation factor measured from the isotope effect experiment varies from 0.781 ± 0.087 to 0.623 ± 0.051 between temperatures of 735 to 906 ° C. Values of 'b' at 860 and 924 ° C are found to be 9.19 and 13.69, respectively. These values are consistent with the vacancy migration mechanism. Isotopieuntersuchungen für die Diffusion von Cd in Silbereinkristallen werden unter Verwendung des Isotopenpaares Cd^115m und Cd¹⁰⁹ im Temperaturbereich von 730 bis 906° C durchgeführt. Der Verstärkungsfaktor _"b" wird in verdünnten Ag-Cd-Legierungen bis zu ≈ 3 At% Kadmium bei 860 und 924 ° C gemessen. Die Ergebnisse des Isotopieeffekts und des Verstürkungsfaktors werden gemeinsam zur Berechnung der Sprungfrequenzverhältnisse mittels des Howard-Manning-Verfahrens benutzt. Der aus dem Isotopieeffekt gefundene Korrelationsfaktor ändert sich im Temperaturbereich 735 bis 906 ° C von 0,781 ± ; 0,087 auf 0,623 ± ; 0.051. Die Werte von _"b" betragen 9,19 und 13,69 bei 860 bzw. 924 ° C. Diese Werte stimmen mit der Vorstellung der Diffusion über Einfachleerstellen überein.