X-ray diffraction profile analysis for characterizing isothermal aging behavior of M250 grade maraging steel

Abstract

X-ray diffraction (XRD) studies were carried out to characterize aging behavior of M250 grade maraging steel samples subjected to isothermal aging at 755 K for varying durations of 0.25, 1, 3, 10, 40, 70, and 100 hours. Earlier studies had shown typical features of precipitation hardening, wherein the hardness increased to a peak value due to precipitation of intermetallics and decreased upon further aging (overaging) due to reversion of martensite to austenite. Intermetallic precipitates, while coherent, are expected to increase the microstrain in the matrix. Hence, an attempt has been made in the present study to understand the microstructural changes in these samples using XRD line profile analysis. The anisotropic broadening with diffraction angle observed in the simple Williamson-Hall (WH) plot has been addressed using the modified WH (mWH) approach, which takes into account the contrast caused by dislocations on line profiles, leading to new scaling factors in the WH plot. The normalized mean square strain and crystallite size estimated from mWH have been used to infer early precipitation and to characterize aging behavior. The normalized mean square strain has been used to determine the Avrami exponent in the Johnson-Mehl-Avrami (JMA) equation, which deals with the kinetics of precipitation. The Avrami exponent thus determined has matched well with values found by other methods, as reported in literature.