Effect of ageing on the microstructural stability of cold-worked titanium-modified 15Cr-15Ni-2.5Mo austenitic stainless steel

Abstract

A titanium-modified 15Cr-15Ni-2.5Mo austenitic stainless steel conforming to ASTM A 771 (UNS S 38660), commercially called Alloy D9, is being indigenously developed for application as material for the fuel clad and the hexagonal wrapper for fuel subassemblies of the Prototype Fast Breeder Reactor. As this material would be used in the cold-worked condition and would be subjected to prolonged exposure to elevated service temperatures, the effect of ageing on the microstructural stability was studied as a function of the amount of cold work. The material was given 2.5–30% prior cold work and then aged at temperatures in the range 923 to 1173 K for times ranging from 0.25 to 1000 h. Hardness measurements made before and after ageing were correlated with the Larson-Miller parameter to determine the highest stable prior cold-work level. Optical microscopy was used to study the microstructural changes. The influence of prolonged exposure for two and three years at the operating temperatures of clad and wrapper, on the elevated temperature tensile properties of a 20% prior cold-worked Alloy D9 was also studied through accelerated ageing treatments based on the present parametric approach.