Transport properties of lithium and sodium doped nickel oxide

Abstract

The electrical resistivity and thermoelectric power of ceramic samples of NiO doped with Li and Na are studied as function of temperature and dopant concentration. The resistivity α is measured in the temperature range 100 to 700 K and thermoelectric power in the range 100 to 300 K. The results obtained indicate band conduction as the mechanism for transport in NiO. The resistivity and thermoelectric power of Na doped NiO are found to be higher than the corresponding Li doped samples. This result is explained as due to the increased strain in the lattice by the introduction of Na which has a significantly higher ionic radius than nickel. Der spezifische Widerstand und die Thermospannung von Keramikproben von mit Li und Na dotiertem NiO werden in Abhngigkeit von der Temperatur und Dotierungskonzentration untersucht. Der Widerstand ∂ wird im Temperaturbereich 100 bis 700 K und die Thermospannung α im Bereich 100 bis 300 K gemessen. Die erhaltenen Ergebnisse zeigen, daβ der Transportmechanismus in NiO Bandleitung ist. Der Widerstand und die Thermospannung von Na dotiertem NiO ist hoher als in entsprechenden Li-dotierten Proben. Dieses Ergebnis wird mit der erhohten Spannung im Gitter durch die Einfuhrung von Na erklrt, das einen betrchtlich hoheren Ionenradius als Nickel hat.