Rheological behavior of semi-solid slurry of A356 alloy at high shear and cooling rates

Barman, N. ; Dutta, P. (2008) Rheological behavior of semi-solid slurry of A356 alloy at high shear and cooling rates Solid State Phenomena, 141-143 . pp. 409-414. ISSN 1012-0394

Full text not available from this repository.

Official URL: http://www.scientific.net/SSP.141-143.409

Related URL: http://dx.doi.org/10.4028/www.scientific.net/SSP.141-143.409

Abstract

The rheological behavior of semisolid aluminium alloy (A356) slurry is investigated by using a concentric cylinder viscometer under high cooling rate (30 to 50°C/min) and high shear rate (650 to 1500s-1) conditions. Two different series of experiments are carried out. In all of these experiments, the pellets of A356 alloy are poured into the outer cylinder where they melt completely by resistance heating. When the inner cylinder is placed concentrically, the molten metal resides in the annular space between the cylinders. As the inner cylinder rotates, the alloy is sheared continuously during cooling from a temperature of 630°C, and a slurry forms. In the first series of experiments, for different cooling rates, shearing continues under a constant shear rate until rotation of the inner cylinder stops. During experiments, the temperature of the slurry is measured continuously using a K-type thermocouple, from which the solid fraction is calculated. In the second series of experiments, the molten alloy is cooled and sheared continuously at different shear rates for a given cooling rate. The apparent viscosity of the slurry is calculated by measuring the torque applied to the inner cylinder and its rotational speed. The results show that the slurry viscosity increases with increasing fraction of solid and increasing cooling rate, and it decreases with increasing shear rate. At high values of shear and cooling rates, the viscosity varies gradually up to a solid fraction of about 0.5.

Item Type:Article
Source:Copyright of this article belongs to Trans Tech Publications Inc..
Keywords:Apparent Viscosity; Cooling Rate; Semi-Solid Slurry; Shear Rate; Solid Fraction