Ayyub, P. ; Multani, M. ; Barma, M. ; Palkar, V. R. ; Vijayaraghavan, R. (1988) Size-induced structural phase transitions and hyperfine properties of microcrystalline Fe2O3 Journal of Physics C: Solid State Physics, 21 (11). pp. 2229-2245. ISSN 0022-3719

Full text not available from this repository.

Official URL: http://iopscience.iop.org/0022-3719/21/11/014?from...

Related URL: http://dx.doi.org/10.1088/0022-3719/21/11/014

Abstract

Microcrystalline particles of Fe2O3 having different sizes (varying between 70 and 5 nm) have been synthesised using a novel three-component micro-emulsion technique. A succession of crystal-size-induced structural transitions was observed. While alpha -Fe2O3 was found to nucleate for a particle size above 30 nm, gamma -Fe2O3 was preferentially formed for a size below 30 nm, whereas amorphous Fe2O3 was formed at a particle size of 5 nm. These structural transformations have been related to the increase in the unit-cell volume that occurs as the particle size is decreased. The size dependence of the lattice parameter is shown to arise from a coupling of the surface energy to the dilatational lattice mode. A model Hamiltonian which incorporates this interaction and displays size-induced phase transitions is defined. The Mossbauer hyperfine field in the microcrystalline samples at 4.2 K was found to be substantially smaller than in the 'bulk'. The hyperfine parameters of the amorphous sample were found to be similar to those pertaining to samples prepared by conventional techniques such as melt quenching. A large anisotropy in the ionic vibrational amplitudes was detected in samples with particles smaller than about 10 nm.

Item Type:Article
Source:Copyright of this article belongs to Institute of Physics.
ID Code:61494
Deposited On:15 Sep 2011 03:18
Last Modified:12 Jul 2012 04:54

Repository Staff Only: item control page