Polarization reversal studies in ferroelectric TAAP

Abstract

Telluric Acid Ammonium Phosphate (Te(OH)₆2(NH₄)H₂PO₄(NH₄)₂HPO₄) reffered to as TAAP is a recently discovered class m ferroelectric. It undergoes FE-PE transition at 48°C. Switching studies in this crystal has been carried out in the temperature range -14°C to 39°C by applying fields up to 4 kV/cm. Measurements were carried out on (101) plates cut from the crystals grown from solution. X-ray irradiation was carried out at room temperature by means of an X-ray tube operating at 25 kV and 15 mA with copper target. Air drying silver paste was used as electrodes. Samples were checked for hysteresis loop using a modified Sawyer-Tower circuit. The P_s value obtained from the loop is 2.1 µC/cm² which is comparable to the earlier reported value. It was however noticed that the loop was slightly shifted to right with respect to the origin indicating the presence of a small internal bias which was 100 V/cm in the virgin crystal. This bias could not be removed even after repeated crystallization. On irradiation the internal biasing field increased which was indicated by a further shift of the hysteresis loop. The bias seems to saturate at about 750 V/cm for which the crystal had to be irradiated for about 3 hours.