Investigation of the (PEG)_xLiCl system using conductivity, DSC and NMR techniques

Abstract

Electrolytes based on polyethylene glycol (PEG, mol.wt.8000) and LiCl of compositions, (PEG) _xLiCl, x=4, 6, 8, 10, 12, 40, 60, where x is the O/Li ratio, were prepared by solution casting from methanol solutions. FTIR studies indicate that the ether oxygens of the polymer chain participate in Li⁺ ion conduction. The presence of a salt-polymer complex that melts around 190οC was evidenced by DSC measurements for the electrolytes with compositions x<12. The highest conductivity was obtained at the composition x=10 which was attributed to the presence of a mostly amorphous compound. NMR measurements indicated two regions of motional narrowing, one attributable to the glass transition and another to translational diffusion.