Realization of biferroic properties in La0.6Sr0.4MnO3∕0.7Pb(Mg1∕3Nb2∕3)O3–0.3(PbTiO3) epitaxial superlattices

Roy Chaudhuri, Ayan ; Ranjith, R. ; Krupanidhi, S. B. ; Mangalam, R. V. K. ; Sundaresan, A. ; Majumdar, S. ; Ray, S. K. (2007) Realization of biferroic properties in La0.6Sr0.4MnO3∕0.7Pb(Mg1∕3Nb2∕3)O3–0.3(PbTiO3) epitaxial superlattices Journal of Applied Physics, 101 (11). p. 114104. ISSN 0021-8979

Full text not available from this repository.

Official URL: http://doi.org/10.1063/1.2743085

Related URL: http://dx.doi.org/10.1063/1.2743085

Abstract

A set of symmetric and asymmetric superlattices with ferromagnetic La0.6Sr0.4MnO3 (LSMO) and ferroelectric 0.7Pb(Mg1/3Nb2/3)O3-0.3(PbTiO3) as the constituting layers was fabricated on LaNiO3 coated (100) oriented LaAlO3 substrates using pulsed laser ablation. The crystallinity, and magnetic and ferroelectric properties were studied for all the superlattices. All the superlattice structures exhibited a ferromagnetic behavior over a wide range of temperatures between 10 and 300 K, whereas only the asymmetric superlattices exhibited a reasonably good ferroelectric behavior. Strong influence of an applied magnetic field was observed on the ferroelectric properties of the asymmetric superlattices. Studies were conducted toward understanding the influence of conducting LSMO layers on the electrical responses of the heterostructures. The absence of ferroelectricity in the symmetric superlattice structures has been attributed to their high leakage characteristics. The effect of an applied magnetic field on the ferroelectric properties of the asymmetric superlattices indicated strong influence of the interfaces on the properties. The dominance of the interface on the dielectric response was confirmed by the observed Maxwell-Wagner-type dielectric relaxation in these heterostructures.

Item Type:Article
Source:Copyright of this article belongs to American Institute of Physics.
ID Code:120132
Deposited On:23 Jun 2021 06:08
Last Modified:23 Jun 2021 06:08

Repository Staff Only: item control page