Influence of nanoenvironment on luminescence of Eu³⁺ activated SnO₂ nanocrystals

Abstract

The emission intensity of the peak at 612 nm (⁵D₀→⁷F₂) of the Eu³⁺ ions activated SnO₂ nanocrystals (doped and coated) is found to be sensitive to the nanoenvironment. We have compared the luminescence efficiencies of the nanocrystals of SnO₂ doped by Eu₂O₃ with those of SnO₂ coated by Eu₂O₃ and we found that the intensities are significantly higher in coated nanocrystals. Furthermore, it is clear from luminescence intensity measurements that Eu³⁺ ions occupy low symmetry sites in the Eu₂O₃ coated SnO₂ nanocrystal. The analysis suggests that the radiative relaxation rate is higher in Eu₂O₃ coated SnO₂ nanocrystals than Eu₂O₃ doped SnO₂ nanocrystals due to the asymmetric environment of Eu³⁺ ions in coated samples.